Magnesium-zirconium brick is only tried once. The trial part is located on the back of the burning belt. The performance of the brick hanging kiln skin is better, but the kiln skin is too thick, which will cause some influence on the ventilation in the kiln. The application of the transition zone technology of silicon molybdenum tiles determines the most frequent change of the kiln skin, so the anti-stripping performance of refractory bricks is required to be higher. Moreover, since the liquid phase of the zone begins to appear, the thermal load on the refractory bricks increases accordingly. If there is no kiln skin, the bricks in this area are also required to have good resistance to chemical attack and abrasion resistance. The porosity is low, and the resistance to sulfur and alkali corrosion is strong. The thermal shock stability and mechanical strength indexes are all excellent. Silicon brick Mo expansion coefficient is small, in order to prevent the emergence of the new brick masonry or just igniting kiln operation lottery phenomenon, we slightly modify the size of the brick, firebrick size size from the original single brick weight has increased, but It did not cause any impact on the bricklaying work and ensured the safe operation of the kiln system. After silicon molybdenum bricks, the transition period has greatly increased, and in the past two years, there have been no unplanned kiln shutdowns due to brick damage, which has created conditions for improving the kiln operation rate. Because of the better wear resistance of the brick, even in the case of frequent ball kilns in the kiln, there can be a longer life cycle. The brick has better anti-stripping performance, no partial damage of the fire brick will occur during use, the occurrence of a local red kiln accident is prevented, the frequency of brick replacement in the kiln system is reduced, and a certain economic benefit is created for the enterprise. Compatibility: China's refractories standards are basically equivalent to adopting or actively adopting OCT standards, and gradually adopting international standards. Therefore, the revision of this standard is still based on international standards in terms of technical content, taking into account the basic conditions of China's refractory industry, and strive to have a wider compatibility, in order to help improve the competitiveness of China's refractory industry in the international market. Baggage X Ray Machine,Cargo Security Scanner,Air Cargo Scanner,Penetration Luggage Scanner Shenzhen MCD Electronics Co., Ltd. , https://www.gdmcd.com